What to do when industrial casters are degummed or burst

When the industrial caster appeared degumming and bursting, what should he do? During the visit to the client, he encountered a customer who was a mechanical device. When the industrial caster appeared degumming and bursting, he had to contact a customer who was a mechanical device during the visit to the client. He told me that before they used a batch of industrial casters, the wheels were in use. There was a large number of phenomena such as the bursting of caster tires. There was no way to use them, and there was no way to repurchase a batch later. After hearing this case, I had a detailed understanding of its use, as well as a parameter of this aspect of the industrial caster, and a situation of the company to know that the industrial caster could not meet the requirements. Because the customer's device is a type that is often mobile-driven, it is prone to degumming or bursting when the load-carrying time is too long. Generally speaking, if the industrial universal wheels used by customers are often moved and driven, then we have to carry out weighted walking tests on these industrial casters for sampling before leaving the factory, or if customers have special requirements, they will perform Testing, in order to prevent the production of inferior products to improve the quality of industrial casters, so an industrial caster manufacturer is critical to the quality of the product. Degumming and bursting of industrial casters should enhance the inspection of product quality. Industrial caster weight walking wear test: 1, test purpose: test production of industrial caster meets the requirements to ensure product quality. 2, the ambient temperature: no special environmental requirements, the general indoor environment can be. 3, test equipment: caster multi-functional testing machine. 4. Height of Walking Obstacles: The soft wheels are 3% of the wheel diameter, and the hard wheels are not. The obstacles and the direction of wheel walking are at an Angle of 45°. Two obstacles are alternately placed. 5. Timing of testing: After cooling by single round of injection molding, the brackets are riveted to complete the assembled product. 6, tread hardness: TPU (85A-100A), TPE/TPR (65A-90A) 7, test standards: The main implementation of customer requirements. 8, all normal production of randomly sampled products in accordance with the conventional carrying capacity of 1.2 times the load, walking for 5 hours; incoming test according to the conventional carrying capacity of 1.2 times the weight, continuous walking 8 hours, tires without cracks, peeling and local excessive wear; There is no abnormal damage to the parts of the industrial universal wheel and permanent deformation that affects its use. The bearings (sets) rotate normally, without looseness and jamming. The advantages of industrial caster weight walking test are many, and it can detect a long service life of this caster. Under the same production process, industrial casters produced by different materials can be detected and contrasted, and the caster material can be distinguished. With bad. Under the current environment driven by this interest, some industrial caster manufacturers have used back materials to reduce their own costs (some recycled materials have been recycled many times, their toughness is very poor, and they are easily disconnected). There are many burrs, and the more difference is poor transparency, dull color, poor elasticity, poor high temperature resistance, and easy to break. Therefore, these factors can cause the overall performance of industrial casters to deteriorate. As buyers and consumers, they should strengthen their awareness in this area in order to better protect their own rights and interests: